搜索结果: 1-8 共查到“有机高分子材料 Si”相关记录8条 . 查询时间(0.283 秒)
Studying of polyoxadiazole with Si atom in the backbone
UV-Vis spectroscopy AFM microscopy IR spectroscopy Spin-coating method Organic polymer
<
2010/8/17
An application of organic polymers as thin films in optoelectronic devices is wide enough. The most common in this area are semiconducting polymers as polyparaphenylenevinylene (PPV) [1] and polyparap...
新型耐热材料—含Si链金属有机高分子
Si链 金属有机高分子 耐热材料
<
2008/12/5
聚合物材料在现代科学技术中起着很重要的作用,但目前常规聚合耐热性尚不理想,C-C键在250℃以下就会发生断裂。为得到能在400℃左右使用的聚合物,含Si链金属有机高分子是一个很好的发展方向。含Si链金属有机高分子可用于耐热电线、耐热涂料、耐热粘结剂、SiC、TRF纤维的前驱体的开发等方面。对含金属的聚硅烷高分子,课题组已用硅烷单体预聚物与Ti、Zr、V、Al、Fe、Co、Sn、As、Mg、Pb和S...
Corrosion resistance of Si–Al-bearing ultrafine-grained weathering steel
corrosion weathering steel ultrafine grain rust aluminum silicon
<
2010/10/13
In the Ultra-steel project at the National Institute for Materials Science (NIMS), which run
from 1996 to 2005, high-Si–Al-content ultrafine-grained (UFG) weathering steel was
developed by grain ref...
Mo原子溅射能量对Mo/Si薄膜晶相的影响
<
2007/12/18
摘要 用磁控溅射法制备了Mo/Si薄膜,用AFM和XRD分别研究了Mo原子的溅射能量不同时,Mo/Si薄膜表面形貌和晶相的变化。通过比较发现,随着Mo原子溅射能量的增大,Mo/Si薄膜表面粗糙度增加,Mo和Si的特征X射线衍射峰也越来越强,并且Mo膜层和Si膜层之间生成了MoSi2。Mo原子的溅射能量是诱导非晶Si结晶和MoSi2生成的主要原因。
锂离子电池 Si-Mn/C负极材料的电化学性能
<
2007/12/13
摘要 利用机械球磨法得到Si和Mn原子比为3: 5的复合材料, 将此材料与20 wt%的石墨混合球磨得到Si3Mn5/C复合材料. 利用X射线衍射(XRD)和扫描电子显微镜(SEM)分析材料的物相和电极的微观结构. 结果表明: 所得材料中没有Si-Mn二元新相的生成, 材料的颗粒尺寸为0.5~2.0μm. 碳的加入抑制了活性中心Si在循环过程中的较大结构变化, 且Si-Mn复合物颗粒均匀地分散在碳...
Si-TaSi2共晶自生复合场发射材料的定向凝固组织特征
<
2007/12/12
摘要 采用电子束悬浮区熔装置(EBFZM)制备了Si-TaSi2共晶自生复合场发射材料, 系统地研究了Si-TaSi2共晶的定向凝固组织特征. 当凝固速率在0.3~9.0mm/min范围内变化时, 均可获得Si-TaSi2共晶自生复合材料, 具有高精确取向的TaSi2纤维在硅连续基体中均匀分布. 随着凝固速率的增大, TaSi2纤维的直径和平均间距减小, 面密度和体积分数增大. 采用零功率法考察了...
低比电阻Si-Ti-C-O纤维先驱体的合成
比电阻 Si-Ti-C-O纤维 先驱体 合成
<
2007/10/26
文章摘要:
通过液体聚硅烷(LPS)与钛酸四丁酯Ti(OBu)4反应合成了不同钛含量的聚钛碳硅烷先驱体, 经熔融纺丝、不熔化处理及高温烧结等工艺制备出比电阻为10^6~10^3Ω•cm的Si-Ti-C-O纤维.用IR、GPC、VPO、TG、DTA等方法分析研究了聚钛碳硅烷的组成、结构与特性及其与含钛量的关系.